Thermal behavior of ethylene copolymers with di- and tri-alkenylsilsesquioxane comonomers synthesized by post-metallocene catalysts
2020
AbstractThis paper reported thermal properties of ethylene copolymers with di- and tri-alkenylsilsesquioxanes (POSS) synthesized by bis(phenoxy-imine) Ti, Zr, V, and V salen-type complexes. Ethylene copolymers with multi-alkenyl POSS obtained by such complexes contain multi-alkenyl POSS incorporated into the polymer chain as a side group. They were characterized by different thermal behavior depending on the kind of multi-alkenyl POSS comonomer, and type of the catalyst used, as well as polymerization conditions and thus the structure of the copolymer chain. Ethylene/POSS copolymers differed in incorporation of POSS into the polymer chain, content of specific unsaturation groups, and molecu…
Thermal stability of ethylene copolymers with multi-alkenylsilsesquioxane comonomers synthesized by organometallic catalyst - Effect of copolymer str…
2020
Abstract This study was focused on thermal properties of ethylene copolymers with di-, tri- and tetra-alkenylsilsesquioxanes (POSS) synthesized by ansa-metallocene complex. Ethylene copolymers with multi-alkenyl POSS were characterized by different thermal behavior depending on the kind of POSS comonomer and its content, as well as the copolymer structure. The copolymers differed in the incorporation way of POSS into the polymer chain (linear and crosslinked structure), content of specific unsaturation groups, molecular weight, as well as heterogeneity of polymer chain compositions. It was found that the kind and content of unsaturation groups in E/POSS copolymers played a significant role …
The effect of macromolecular architecture of ethylene copolymers with multi-alkenylsilsesquioxane on morphological, rheological and dynamic mechanica…
2021
Abstract The influence of the degree and the way of incorporation of multi-alkenylsilsesquioxane into the polymer chain on morphological, rheological and dynamic mechanical parameters were determined. It was found that POSS incorporated into the polymer chain was located outside the crystalline structure of lamella in amorphous phase. The incorporation of POSS-6-2 as a pendant group resulted in significant increase of separation of macromolecules. The key factor in rheological and dynamic mechanical behavior of copolymers turned out to be the way of POSS incorporation into the polymer chain. The incorporation of POSS into the polymer chain as a pendant group resulted in decreased relaxation…